Cevian®-V UG10
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3p0skz_Cevian--V-UG10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V UG10 is an acrylonitrile butadiene styrene (ABS) product, which contains a 10% glass fiber reinforced material. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 68.6 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 3730 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 117 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Additional Information |
|---|
| Specific Gravity, ASTM D792, 73°F, 50% RH: 1.11Water Absorption, ASTM D570, 73°F, 24 hr: 0.3 % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 210 - 230 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 48.3 - 117 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SuperKleen 3003-85 CLEAR 0003 | AlphaGary | PVC, Flexible | SuperKleen |
| NYLAFORCE® A 50 TS13 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | NYLAFORCE® |
| INEOS PP H12Z-03 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| LG PMMA IH830C | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| POLYCASA® ACRYL KR 2006/1 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |