LNP™ THERMOCOMP™ OCF62E compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3o9rRM_LNP-THERMOCOMP-OCF62E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OCF62E is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding Also known as: LNP* THERMOCOMP* Compound OCF-1008 EM Product reorder name: OCF62E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.40 | % | |
| Across Flow : 24 hr | 0.70 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 30300 | MPa | ASTM D638 |
| -- | 28600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 157 | MPa | ASTM D638 |
| Yield | 133 | MPa | ISO 527-2/5 |
| Break 3 | 157 | MPa | ASTM D638 |
| Break | 133 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 0.74 | % | ASTM D638 |
| Yield | 0.56 | % | ISO 527-2/5 |
| Break 5 | 0.74 | % | ASTM D638 |
| Break | 0.56 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 19100 | MPa | ASTM D790 |
| -- 7 | 20600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 46.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 206 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 63 | J/m | ASTM D256 |
| 23°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D4812 |
| 23°C 11 | 14 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 280 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 281 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 267 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 268 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.0E-6 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 1.0E-6 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.6E-6 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 4.6E-6 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ME-2259DN | Teknor Apex Company | TPE | Sarlink® TPE |
| Xuchuan XCW-8066L | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Dryflex® 500600S | ELASTO | SEBS | Dryflex® |
| POLYFLAM® RPP 1058UH | A. Schulman Inc. | PP, Unspecified | POLYFLAM® |
| LNP™ LUBRICOMP™ ZP001XXP compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |