POCAN® AF 4130 000000
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3nu0T2_POCAN-AF-4130-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+ASA, 30% glass fibers, injection molding, flame retardant, low tendency to warp |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.61 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 0.80 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.40 | % | |
| Flow : 260°C, 2.00 mm 3 | 0.30 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10000 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 180 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.2 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT+ASA, GFMR, 09-110, GF30; ISO 1043- PBT+ASA GF FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 187 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/B50 |
| Melting Temperature 8 | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 800 | °C | |
| 1.50 mm | 800 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1403 P | RTP Company | PPSU | RTP |
| Unilex™ UP 8020NS | United Polychem | PP Homopolymer | Unilex™ |
| BMC 615 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| INSTRUC TPUGF10 60D | Infinity LTL Engineered Compounds | TPU, Unspecified | INSTRUC |
| POCAN® BF 4215 000000 | LANXESS Corporation | PBT | POCAN® |