Borealis PP ZC011
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3nRstY_Borealis-PP-ZC011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZC011 is a Mineral filled polypropylene compound intended for extrusion moulding. The product is 30% Mineral filled. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 2.3 | kJ/m² | ISO 180/1A |
| 0°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability (1.00 mm) | 100 | mm/min | ISO 3795 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 230 | °C | |
| Melt Temperature | 200 - 230 | °C | |
| Die Temperature | 200 - 230 | °C |
| Extrusion instructions |
|---|
| Head Temperature: 200 - 230 °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E890 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Integra™ PC 5027 F1 | PolySource, LLC | PC | Integra™ PC |
| Iupilon® GSH2010LR Y082 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| ESTOPLAST XU 6100BB01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| ULTEM™ 2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |