Electrafil® PA6 GF20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3n7N1G_Electrafil-PA6-GF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®PA6 GF20 is a polyamide 6 (nylon 6) product, which contains 20% glass fiber reinforced materials and fillers. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 - 1.0E+7 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1312 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Sinvicomp SRF1807 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Ferro PP LPP10BK72NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Perlast® G90A | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| LEXAN™ 3413R resin | SABIC Innovative Plastics | PC | LEXAN™ |