Zenite® ZE55201
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Zenite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3n6Dlo_Zenite-ZE55201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zenite® ZE55201 is a 50% mineral/glass fiber reinforced liquid crystal polymer for injection molding. and It is specifically suitable for applications requiring ultra flatness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.85 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 88.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 165 | MPa | ISO 178 |
| Compressive Stress (1% Strain) | 21.3 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.6 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 300 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 290 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.031 | IEC 60250 | |
| 1 MHz | 0.031 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Oxygen Index | 41 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density of Melt | 1.620 | g/cm³ | Internal method |
| Ejection Temperature | 270 | °C | Internal method |
| Specific Heat Capacity of Melt | 1500 | J/kg/°C | Internal method |
| Thermal Conductivity of Melt | 0.40 | W/m/K | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 335 - 345 | °C | |
| Front Temperature | 335 - 345 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 330 - 350 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 40 to 60°CZone 4 Temperature: 335 to 345°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 1203-30 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| TEKNIFLEX® VA10200 ALU | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| PERLER® O08U1000B10 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| Sylvin 8250-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CERTENE™ LG790 | Muehlstein | ABS | CERTENE™ |