TECHNO AES W240
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | TECHNO AES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3mLWhK_TECHNO-AES-W240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNO AES W240 is an Acrylonitrile Ethylene Styrene (AES) product. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 105 | ASTM D785 | |
| R-Scale | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 49.0 | MPa | ASTM D638 |
| Yield | 48.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2450 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.4 | MPa | ASTM D790 |
| -- | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 18 | kJ/m² | ISO 179 |
| Notched Izod Impact | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000/508 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Borlink™ LE0315-99 | Borealis AG | TP, Unspecified | Borlink™ |
| Flontech® FT-1-TUR-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Latimass 52/11-04 D008 | LATI S.p.A. | PP Homopolymer | Latimass |
| Karina WHITE PVC COMPOUND -E 839-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |