ARCEL® 730 (1.50 pcf)
| Category: | PS+PE , Polystyrene + PE |
| Manufacturer: | NOVA Chemicals |
| Trademark: | ARCEL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3mGcVG_ARCEL-730-1-50-pcf-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ARCEL® 730 (1.50 pcf) is a Polystyrene + PE (PS+PE) material. It is available in North America for foam processing. Typical application of ARCEL® 730 (1.50 pcf): Foam |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0240 | g/cm³ | ASTM D3575 |
| Particle Size - 98% | 0.800 to 1.70 | mm | |
| VOC Content | |||
| Pentane | 11 | % | |
| Plasticizer | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain | 12 | % | ASTM C203 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture | 168 | N | ASTM D3763 |
| Tear Strength - at Maximum Load | 1.8 | kN/m | ASTM D3575 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 0.338 | MPa | ASTM D3575 |
| Flexural Strength | ASTM C203 | ||
| -- | 0.289 | MPa | |
| 5.0% Strain | 0.238 | MPa | |
| Compressive Strength | ASTM D3575 | ||
| 10% Strain | 0.117 | MPa | |
| 25% Strain | 0.144 | MPa | |
| 50% Strain | 0.198 | MPa | |
| 75% Strain | 0.449 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 2200-15 CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Shin-Etsu Elastomer KE-971TU | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Staramide AST43 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Chemlon® 60GF3 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| POLYFLAM® SDR 5000 | A. Schulman Europe | PS (GPPS) | POLYFLAM® |