DOW™ LDPE 692 LDPE HEALTH+™
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3mEbMK_DOW-LDPE-692-LDPE-HEALTH-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ LDPE 692 HEALTH+™ is a Low Density Polyethylene barefoot resin designed for extrusion blow molding, injection blow molding, and blow-fill seal applications with good flexibility, moderate rigidity and good chemical resistance. It is also suitable for medical packaging films. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 4.96 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 197 | J/cm³ | ASTM D882 |
| TD : 51 µm | 211 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.6 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 11.4 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 29.7 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 28.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 480 | % | ASTM D882 |
| TD : Fracture, 51 µm | 680 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 280 | g | ASTM D1922 |
| TD : 51 µm | 350 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 112 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 70 | ASTM D2457 | |
| Haze (50.8 µm) | 8.6 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：单跨双混合 模具间隙：40 密尔 (1.0 mm) 熔体温度：446 °F (230 °C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：88 rpm 冷冻线高度：23.5 英寸 (597 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P601-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Varcum 92600 | Durez Corporation | Phenolic | Varcum |
| Keyflex® BT 1040D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Hostacom ERC 342N E1 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| KEBAFLEX® E D 50.1 | BARLOG plastics GmbH | TPV | KEBAFLEX® |