LNP™ THERMOCOMP™ EC006E compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3lz4Ir_LNP-THERMOCOMP-EC006E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* EC006E is a compound based on Polyetherimide resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive Also known as: LNP* THERMOCOMP* Compound EC-1006 EM Product reorder name: EC006E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.51 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.17 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 23300 | MPa | ASTM D638 |
| -- | 18500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 231 | MPa | ASTM D638 |
| Break | 215 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.5 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 19200 | MPa | ASTM D790 |
| -- | 20800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 315 | MPa | ASTM D790 |
| -- | 306 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.52 | ||
| vs. Itself - Static | 0.48 | ||
| Wear Factor - Washer | 75.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 6.30 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 206 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 208 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G0 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Sarlink® TPV X6145N | Teknor Apex Company | TPV | Sarlink® TPV |
| NuSil MED-4135 | NuSil Technology | Rubber | NuSil |
| Braskem PP RP 350 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Durethan® BM 40 X H2.0 EF 900116 | LANXESS GmbH | Nylon 6 | Durethan® |