NORYL GTX™ GTX6203 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3lfi0P_NORYL-GTX-GTX6203-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX6203 is a 20% talc filled material with superior dimensional stability, excellent processability and surface appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.60 - 0.90 | % | Internal method |
| Transverse flow : 3.20mm | 0.60 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4600 | MPa | ASTM D638 |
| -- | 4900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 65.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2/5 |
| Fracture 5 | 3.0 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/5, ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3800 | MPa | ASTM D790 |
| -- 7 | 4000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 50 | J/m | ASTM D256 |
| 23°C | 60 | J/m | ASTM D256 |
| -30°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 12(23°C) | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 190 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 13 | 190 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ASTM D1525 14 |
| -- | 190 | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.26 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SA131 | RJM International, Inc. | PC+PBT | RJM |
| Clariant Nylon 6/6 6604G33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Karina CLEAR PVC COMP. -E 70/236-DA-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucky Enpla LPC100F | Lucky Enpla Co LTD | PC | Lucky Enpla |
| Sylvin 8215-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |