Idemitsu PS HT55
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Idemitsu PS |
| Trademark: | Idemitsu PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3kx1UU_Idemitsu-PS-HT55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Idemitsu PS HT55 is a high impact polystyrene product,. It can be processed by extrusion or injection molding and is available in the Asia-Pacific region. Typical application areas are: housing. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 56 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 31.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 1960 | MPa | ASTM D790 |
| Flexural Strength | 54.9 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 80 | ASTM D2457 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 12 kg-cm/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 190 - 220 | °C | |
| Front Temperature | 210 - 240 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 200 - 240 | °C | |
| Cylinder Zone 4 Temp. | 200 - 240 | °C | |
| Die Temperature | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTODUR® GF20-FR3 | Evonik Industries AG | PBT | VESTODUR® |
| BUP 630 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| Karina WHITE PVC COMPOUND 811-10/ 23-A-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ EL002 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| Mafill® HT 4102 | Ravago Group | PP Homopolymer | Mafill® |