Lastilac 10
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lastilac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3kvC53_Lastilac-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS/PC. Very good brightness and surface appearance. Very good impact resistance. Fair thermal resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 to 0.75 | % | |
| Flow : 2.00 mm | 0.55 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2500 | MPa | |
| 60°C | 2200 | MPa | |
| 90°C | 1900 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Yield, 60°C | 50.0 | MPa | |
| Yield, 90°C | 25.0 | MPa | |
| Break, 23°C | 55.0 | MPa | |
| Break, 60°C | 45.0 | MPa | |
| Break, 90°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 5.0 | % | |
| Yield, 60°C | 4.0 | % | |
| Yield, 90°C | 6.0 | % | |
| Break, 23°C | 40 | % | |
| Break, 60°C | 45 | % | |
| Break, 90°C | 55 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 650 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 75.0 | °C | |
| Vicat Softening Temperature | 110 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 25 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-28177 | Teknor Apex Company | TPE | Monprene® |
| VICTREX® PEEK 650PF | Victrex plc | PEEK | VICTREX® PEEK |
| AURAMID PA6GF35BK ULT | Aurora Manufacturing Ltd | Nylon 6 | AURAMID |
| Elastollan® B 64 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Plexiglas® V825NA | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |