KPOL-PP K-PHC 18.0 B

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3ihpYA_KPOL-PP-K-PHC-18-0-B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is a homopolymer and copolymer of Blenda heterophasic ethylene and propylene; specially designed for injection molding applications generally requiring excellent balance of properties between rigidity and impact resistance. This product has excellent processability and productivity.

Applications

Injection Molding, Automobile Applications, Battery case ; Toys; Household Appliances in general; Crates; Buckets; Base resin for compounding ; High impact resistance parts.

It exhibits a good fluidity combined with a good balance of impact and stiffness as well as a low warpage tendency. Even at sub-zero temperatures and also provides good surface properties and excellent processability.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant BPA Free Copolymer Good Flow Good Impact Resistance Good Processability Good Stiffness Good Surface Finish Low Temperature Resistant Low Warpage Nucleated
Uses	Appliances Automotive Applications Battery Cases Crates Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	18	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	68		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	20.0	MPa	ASTM D638
Tensile Elongation ²(Break)	7.0	%	ASTM D638
Flexural Modulus - 1% Secant	1000	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	40	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	90.0	°C	ASTM D648
Vicat Softening Temperature	150	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3548	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
NuSil MED-6210	NuSil Technology	Silicone	NuSil
Elastollan® 1180 A	BASF Polyurethanes GmbH	TPU-Polyether	Elastollan®
Kpren 130B	Shandong Xuye New Materials Co., Ltd.	CM	Kpren
Karina BLACK PVC COMPOUND 820-48/ 1-D-AC-BZ	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina