SuperLite® SL551200-100 (4.0mm)
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Azdel, Inc. |
| Trademark: | SuperLite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3iSwzt_SuperLite-SL551200-100-4-0mm-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AZDEL SuperLite SL551200-100 (4.0mm) is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the application (i.e.; adhesive films, barrier films, scrim, tough PP films, non-wovens, reinforcements or just the bare surface.) Typically used in non-structural applications where a very high strength to weight ratio is required, such as automotive headliners, door panels, package shelves, and other interior trim. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.339 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | < 0.020 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638 |
| Tensile Strength | 20.0 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | ASTM D3763 | ||
| 23°C, Energy at Peak Load | 4.50 | J | ASTM D3763 |
| 23°C, Total Energy | 7.60 | J | ASTM D3763 |
| Additional Information |
|---|
| Multi-axial Impact Peak Force, ASTM D3763, 23°C: 900 NMass per unit area, Internal Test Method: 1200 g/m²Flexual Strength, SAE J949: 7.5 MPaFlexual Modulus, SAE J949: 1000 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 1009 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| Mirathane™ E380 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| REXtac® APAO RT 2385 | Huntsman Corporation | PAO | REXtac® APAO |
| Stanyl® ForTii™ F12 | DSM Engineering Plastics | Nylon 4T | Stanyl® ForTii™ |
| DINAPLEN® PPH1S07 G30 | Grupo Repol | PP Homopolymer | DINAPLEN® |