Order Products : sales@su-jiao.com
Mecoline S TP 1003 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3iG0t8_Mecoline-S-TP-1003-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen-free, low smoke, thermoplastic, highly flame retardant compound for the sheathing of low and medium voltage cables in General Installation applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | IEC 811-1-3 |
| Water Absorption | |||
| after 240h at 70°C | 1.17 | mg/cm² | IEC 811-1-3 |
| after 24h at 23°C | 0.0650 | mg/cm² | ASTM D570 |
| pH | > 5.3 | IEC 60754-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion | 181 | mm³ | VDE 0472 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test | IEC 811-3-1 | ||
| penetration 6h at 100°C | 9.0 | % | |
| penetration 6h at 90°C | 5.0 | % | |
| Temperature Index | 300 | °C | ASTM D2863 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | < 8.40 | µS/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Smoke Density | ASTM E662 | ||
| Flaming mode | 150 | ||
| Non-flaming mode | 290 | ||
| Toxicity | 1.10 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 4.50 | MPa | BS 6469 99.1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 140 to 160 | °C | |
| Extruder Screw L/D Ratio | 20.0:1.0 to 25.0:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.2 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 140°C) | 35 | MU | DIN 53523 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 53 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 11.7 | MPa | IEC 811-1-1 |
| Tensile Strain (Break) | 200 | % | IEC 811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 811-1-2 | ||
| 100°C, 240 hr | 13 | % | |
| 110°C, 168 hr | 7.3 | % | |
| Change in Tensile Strain at Break in Air | IEC 811-1-2 | ||
| 100°C, 240 hr | -14 | % | |
| 110°C, 168 hr | -14 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1 | 2.5E+12 | ohms·cm | DIN VDE 0303 |
| Dielectric Constant (50 Hz) | 4.80 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 0.080 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 40 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 90.0 to 110 | °C | |
| Cylinder Zone 2 Temp. | 105 to 125 | °C | |
| Cylinder Zone 3 Temp. | 120 to 140 | °C | |
| Cylinder Zone 4 Temp. | 120 to 140 | °C | |
| Cylinder Zone 5 Temp. | 130 to 150 | °C | |
| Adapter Temperature | 135 to 155 | °C | |
| Die Temperature | 150 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | 16h at 20°C, 500V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-13N(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Witcobond® 418-49 | Chemtura | PUR-Ester | Witcobond® |
| ICORENE® 1741 | ICO Polymers EMEA, A Division of A. Schulman | mHDPE | ICORENE® |
| Karina GRAY PVC COMPOUND 801-18/489-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pearlthane® 11T60D | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |