Wellamid® GF10-66/6-LI6-NBK4
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3i13pq_Wellamid-GF10-66-6-LI6-NBK4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Wellamid® GF10-66/6-LI6-NBK4 is a Polyamide 66/6 Copolymer (Nylon 66/6) material filled with 10% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary attribute of Wellamid® GF10-66/6-LI6-NBK4: Impact Modified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.70 to 1.1 | % | |
| Flow : 23°C | 0.90 to 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 7.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 160 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravathane R130A75 | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. | TPU-Polyester | Ravathane |
| Shuman PS 810 | Shuman Plastics, Inc. | PS (HIPS) | Shuman PS |
| Nycal™ 2155R14T1 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Akulon® F132 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Flexirene® FG 23 U | Versalis S.p.A. | LLDPE | Flexirene® |