CERTENE™ HHP-1244
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3hWeRi_CERTENE-HHP-1244.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HHP-1244 is a certified prime, natural color base hexene-copolymer grade, designed for EXTRUSION of PIPE. HHP-1244 meets PE-3408 non-pressure and pressure pipe service requirements from 1 to 64 inch sized diameters and features good long-term hoop strength performance for applications including municipal potable water pipe, fuel gas pipe, re-lining pipe, industrial and mining pipe, storm and sanitary pipe. HHP-1244 processing temperature is 365° to 390°F (185° to 199°C). HHP-1244 meets all requirements of ASTM-D4976 - PE 235 & NSF Standard 14/61. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.944 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.12 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 12 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1(100°C, 1.75mm, 100% Igepal, molding, F50) | > 1000 | hr | ASTM D1693C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Compression Molded) | 22.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | > 500 | % | ASTM D638 |
| Flexural Modulus - 2% Secant 4(Compression Molded) | 960 | MPa | ASTM D790 |
| Slow crack propagation PENT | 150 | hr | ASTM F1473 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Unit classification | PE 345464A | ASTM D3350 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Test specimens from compression molded plaque according to ASTM D 1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 185 - 199 | °C |
| Note Message | |
|---|---|
| 1 . | Notched Bent Strip |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN J-570S | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| Alpha PVC GW 3035-VW1 NATURAL LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Forprene® 6K5901A75VS2 | SO.F.TER. SPA | TPV | Forprene® |
| Lionpol IM-35078 | Lion Polymers Incorporated | TPE | Lionpol |
| LNP™ LUBRICOMP™ RFL33 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |