MAXAMID™ PA66MG40-NC010
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Pier One Polymers, Inc. |
| Trademark: | MAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gvSdY_MAXAMID-PA66MG40-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MAXAMID™ PA66MG40 is also available in black, internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 121 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7930 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 240 | °C | ASTM D648 |
| Melting Temperature | 255 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 290 to 305 | °C | |
| Mold Temperature | 65.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® FEP 9302 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| SLOVAMID® 6 GF 30 LS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Nucrel® 30907 | DuPont Packaging & Industrial Polymers | EAA | Nucrel® |
| AKROMID® B3 GF 25 1 natural (2463) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Karina CLEAR PVC COMPOUND 90/211-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |