DOWLEX™ 6000G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gskRk_DOWLEX6000G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX* 6000G Polyethylene Resin is an ethylene, 1-octene copolymer, suitable for high performance blown film applications, alone or in blends with LDPE. It offers superior seal performance at high extrusion output rates and an excellent balance of optical and mechanical properties. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.916 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD | 100 | MPa | ISO 527-3 |
| 2% secant, TD | 107 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm | 5.40 | MPa | ISO 527-3 |
| TD : Yield, 50 µm | 7.20 | MPa | ISO 527-3 |
| MD : Break, 50 µm | 36.7 | MPa | ISO 527-3 |
| TD : Break, 50 µm | 37.6 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 570 | % | ISO 527-3 |
| TD : Break, 50 µm | 640 | % | ISO 527-3 |
| Dart Drop Impact (50 µm) | 980 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 860 | g | ASTM D1922 |
| TD : 50 µm | 1100 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 1 | 96.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 66 | ASTM D2457 | |
| Clarity (50.0 µm) | 99.0 | ASTM D1746 | |
| Haze (50.0 µm) | 8.5 | % | ISO 14782 |
| Extrusion instructions |
|---|
| Fabrication Conditions for Blown Film Resin: Melt Temperature: 190 to 240°C Blow-Up Ratio: 1.5 to 3.1 Recommended Gauge Range: 10 to150 µm |
| Note Message | |
|---|---|
| 1 . | Compression moulded samples |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8215-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wellamid® MRGF25/15 22H-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| COSMOTHENE® EVA D5010 | TPC, The Polyolefin Company (Singapore) Pte Ltd | EVA | COSMOTHENE® EVA |
| Elastron® G G401.A25.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Eltex® P KS001PF | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |