LNP™ THERMOCOMP™ UF008H compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3gdaRs_LNPTHERMOCOMPUF008Hcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* UF008H is a compound based on Polyphthalamide resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound UF-1008 Product reorder name: UF008H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.27 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.27 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.42 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16100 | MPa | ASTM D638 |
| -- | 14300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 237 | MPa | ASTM D638 |
| Fracture | 205 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.1 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 13400 | MPa | ASTM D790 |
| -- | 13800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 311 | MPa | ASTM D790 |
| -- | 322 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| 23°C 2 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 870 | J/m | ASTM D4812 |
| 23°C 3 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.10 | J | ASTM D3763 |
| -- | 2.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 282 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 272 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 - 321 | °C | |
| Middle Temperature | 316 - 327 | °C | |
| Front Temperature | 327 - 338 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVALAC RX®862A | Vyncolit N.V. | Phenolic | NOVALAC |
| Hypro® PP-CP 4/2 | Entec Polymers | PP Impact Copolymer | Hypro® |
| Karina MBPEB WHITE -E 1000/00856-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Perfactory® ABflex | EnvisionTEC, Inc. | Acrylic, Unspecified | Perfactory® |
| MARPOL® Homo 13.F | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |