Petrotene® PP A1 BRCA001 PH104 MSP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3f0Fad_Petrotene-PP-A1-BRCA001-PH104-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene standard for injection molding. |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 1600 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 50.0 to 60.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 to 155 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 15.0 to 45.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL ABS-GP-IM | Polymer Resources Ltd. | ABS | PRL |
| Hapflex™ 573 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Leona™ 91G55 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Jianqiao PPGF30 | Shanghai Jianqiao Plastic Co., Ltd. | PP, Unspecified | Jianqiao |
| Hifax CA 1168 A 3001 S1 | LyondellBasell Industries | PP Copolymer | Hifax |