Rilsan® BESNO P40 W6 TL
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3egEFu_Rilsan-BESNO-P40-W6-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® BESNO P40 W6 TL is a polyamide 11 produced from a renewable source. This natural grade is plasticized and designed for extrusion. This grade is classified as Halogen free Flame Retardant (HFFR). MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 68 | ||
| Shore D, 15 sec | 60 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 540 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | |
| Break | 32.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 41 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 470 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 181 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA11-P, EFHL, 22-005 | ISO 1874 | |
| Renewable Carbon Conent | > 79 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 210 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ TH-418.S001 6770 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Ferro PP TPP30WA09NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Karina GRAY COLOR CONCENTRATE -E 18/ 35-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1105-7018/GN | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Petrothene® L2560S | LyondellBasell Industries | LDPE | Petrothene® |