| F10G15 is GF 15% reinforced Polybutylene terephthalate(PBT). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 93.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3 | 4900 | MPa | ASTM D790 |
| Flexural Strength 4 | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 220 | °C | ASTM D648 |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 60.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Speed: 40 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFW6500S | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ASTALON™ S2000 | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| DENKA POVAL K-05 | Denka Company Limited | PVOH | DENKA POVAL |
| HiFill® ABS/PBT 1002 GF20 | Techmer Engineered Solutions | ABS | HiFill® |
| Karina LILAC COLOR CONCENTRATE -E 34/ 20-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |