SABIC® PPcompound 57F9722
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3crGEb_SABIC-PPcompound-57F9722.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 57F9722 is an esthetic UV stabilized automotive exterior grade. This talcum filled copolymer combines good scratch resistance with high stiffness and good thermal dimensional stability. SABIC® PPcompound 57F9722 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 28.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 22.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 45 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 16 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 2.3 | kJ/m² | |
| 0°C, Injection Molded | 3.5 | kJ/m² | |
| 23°C, Injection Molded | 7.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 140 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 8.5E-5 | cm/cm/°C | |
| 23 to 80°C | 1.1E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86002-85FUV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unipren® Elastomers B3 NTLA010 75A UP311 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Greene 409 | Greene, Tweed & Co. | Fluoro Si | Greene |
| INEOS HDPE TC46-25 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| LNP™ THERMOCOMP™ LX09404 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |