SUMIKASUPER® LCP E6006LHF
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3cfl6K_SUMIKASUPER-LCP-E6006LHF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.11 | % | ASTM D955 |
| Transverse flow | 0.72 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 158 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.8 | % | ASTM D638 |
| Flexural Modulus | 11200 | MPa | ASTM D790 |
| Flexural Strength | 146 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 380 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 272 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Sumitomo Chemical Method, Machine Direction: 1.1 mils/inMold Shrinkage, Sumitomo Chemical Method, Transverse Direction: 7.2 mils/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 320 - 350 | °C | |
| Front Temperature | 340 - 370 | °C | |
| Nozzle Temperature | 340 - 370 | °C | |
| Mold Temperature | 70.0 - 160 | °C | |
| Injection Pressure | 78.0 - 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 - 39.0 | MPa | |
| Back Pressure | 0.980 - 4.90 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 HS UV | RTP Company | Nylon 66 | RTP |
| Americas Styrenics EA3400 | Americas Styrenics LLC | PS (GPPS) | Americas Styrenics |
| ICORENE® N4450 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |
| Kazan LDPE 102-12K | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| LNP™ THERMOCOMP™ OCF62E compound | SABIC Innovative Plastics | PPS, Branched | LNP™ THERMOCOMP™ |