TRIBOCOMP® A-5 TS0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3cMKYI_TRIBOCOMP-A-5-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® A-5 TS0 is a Polyamide 66 (Nylon 66) product filled with 45% long glass fiber and 10% ptfe fiber. It is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.60 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 16800 | 13000 | MPa | |
| 90°C | 11700 | -- | MPa | |
| 120°C | 8800 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 225 | 170 | MPa | |
| Yield, 90°C | 160 | -- | MPa | |
| Yield, 120°C | 135 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 2.5 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 14000 | 10500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 360 | 270 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | |||
| vs. Itself - Dynamic | 0.29 | -- | ||
| vs. Itself - Static | 0.23 | -- | ||
| Wear Factor | 14 | -- | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 80 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 253 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.1E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.33 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 36 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 270 to 300 | °C | |
| Cylinder Zone 2 Temp. | 270 to 300 | °C | |
| Cylinder Zone 3 Temp. | 285 to 300 | °C | |
| Cylinder Zone 4 Temp. | 285 to 310 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 5521 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| VINIKA® T133D | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| Elastollan® 1185A50V | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| GPPC ABS D-180 | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| Latilub 75/4-20T | LATI S.p.A. | PBT | Latilub |