Ultramid® TG7S
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3byW31_Ultramid-TG7S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to be made of an engineering plastic as opposed to metal. TG7S exhibits improved strength,stiffness and notched impact properties over Ultramid 8333G HI. Applications Include cushion seat pan/frame and other automotive seating applications, automotive fan, power tools and trimmer components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Break, -40°C | 251 | MPa | |
| Break, 23°C | 170 | MPa | |
| Break, 80°C | 97.0 | MPa | |
| Break, 121°C | 77.0 | MPa | |
| Tensile Strain (Break, 23°C) | 3.3 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 23 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 18 | kJ/m² | |
| 23°C | 26 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 203 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SINOF DH-F22E-2 | SINOF HI-TECH MATERIAL CO. LTD | PVDF | SINOF |
| Sylvin 8948-50 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trilene FreeFlow™ 66 | Lion Copolymer, LLC | EPM | Trilene FreeFlow™ |
| Trexlink™ 4780 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| PENTAMID B GV15 GK15 H black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |