Category: | LLDPE , Linear Low Density Polyethylene |
Manufacturer: | POLYMAT |
Trademark: | Prixene® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 3bmEVd_Prixene-EM050E36.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Prixene® EM050E36 is a Linear Medium Density Polyethylene resin of ethylene-hexene copolymer that offers high performance and excellent processability. The applications of this product are in bags, stretch film, co-extruded and monolayer film, coatings, packaging in general. The features presented are a good power, stretching and bending. The product form is in pellets. LLDPE for blow film. The material complies with FDA regulation title 21.CFR177.1520 (. C) 3.1 (a) and 3.2a |
General Information | |
---|---|
Features |
|
Uses |
|
Agency Ratings |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 0.936 | g/cm³ | ASTM D1505 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 1(Yield) | 17.9 | MPa | ASTM D638 |
Tensile Elongation 2(Break) | 650 | % | ASTM D638 |
Flexural Modulus - 1% Secant | 731 | MPa | ASTM D790 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
Vicat Softening Temperature | 118 | °C | ASTM D1525 |
Note Message | |
---|---|
1 . | 51 mm/min |
2 . | 51 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Maxxam™ NR-818.H001-8086 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
Devcon Plastic Steel Putty (A) | Devcon | Epoxy | Devcon |
Karina IVORY PVC COMPOUND -E 360-IS-SI-SD (FREE) (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
OmniCarb™ PC08FR 701 | OMNI Plastics, LLC | PC | OmniCarb™ |
OnForce™ LFT LF0100-5001 NATURAL | PolyOne Corporation | PUR, Unspecified | OnForce™ LFT |