Resinoid 1360HR
| Category: | Phenolic , Phenolic |
| Manufacturer: | Resinoid Engineering Corporation |
| Trademark: | Resinoid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3b5uyK_Resinoid-1360HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resinoid 1360HR is a glass reinforced, two-step phenolic molding compound. It exhibits outstanding impact strength, electrical and thermal properties. It is particularly suitable for high temperature and strength applications. This material comes in pelletized from and is suitable for transfer or compression molding. It can be preformed on automatic equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792A, ISO 1183 |
| Water Absorption | |||
| 24 hr | 0.35 | % | ASTM D570 |
| 23°C, 24 hr | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 67.6 | MPa | ASTM D638 |
| Yield | 68.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 15200 | MPa | ASTM D790 |
| -- | 15000 | MPa | ISO 178 |
| Flexural Strength | 138 | MPa | ASTM D790, ISO 178 |
| Compressive Strength | 169 | MPa | ASTM D695, ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 120 | J/m | ASTM D256A |
| -- | 12 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 360 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | |||
| -- | 130 | kV/mm | ASTM D149 |
| -- | 11 | kV/mm | IEC 60243-1 |
| Additional Information |
|---|
| DTUL @264 psi - Unannealed, ASTM D648: >680°FHDT A (1.80 MPa) Unannealed, ISO 75A-1-2: >360°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ S 218 MZ20 V10 BLACK 2N | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Toyolac® 100 322 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| KRYSTALFLEX™ PE409 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALFLEX™ |
| LNP™ THERMOCOMP™ RC006H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| NORYL™ LS6010 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |