Lushan EJ-1

Category:	HDPE , High Density Polyethylene
Manufacturer:	Guangzhou Lushan New Materials Co., Ltd
Trademark:	Lushan
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3ay2qD_Lushan-EJ-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polyethylene Compounds for Steel Pipe Top Coats Black high density polyethylene compounds Lushan EJ-1 for steel pipe top coats is used as anti-corrosion material for 2PE/3PE buried against-corrosion steel pipe coating system or coated steel plastic composite pipes in the application of oil &gas transportation pipeline and high pressure water pipeline systems. It contains dispersed carbon black with the purpose of excellent weathering properties. HDPE compounds Lushan EJ-1 for steel pipe top coats has good properties such as widely processing range, high Compatibility with adhesive and excellent mechanical properties, etc. HDPE compounds Lushan EJ-1 for steel pipe top coats is designed to meet with requirements of the following National and International standards, under the condition that appropriate industrial processing method are applied under a continuous quality control system and when used in combination with copolymer adhesive resin Lushan L-5R& polyethylene compound top coats EJ-1 and a compatible powder epoxy. NFA 49710 CAN/CSA-Z245.21 DIN 30670S Draft ISO 21809-1

Message

Polyethylene Compounds for Steel Pipe Top Coats

Black high density polyethylene compounds Lushan EJ-1 for steel pipe top coats is used as anti-corrosion material for 2PE/3PE buried against-corrosion steel pipe coating system or coated steel plastic composite pipes in the application of oil &gas transportation pipeline and high pressure water pipeline systems. It contains dispersed carbon black with the purpose of excellent weathering properties. HDPE compounds Lushan EJ-1 for steel pipe top coats has good properties such as widely processing range, high Compatibility with adhesive and excellent mechanical properties, etc.

HDPE compounds Lushan EJ-1 for steel pipe top coats is designed to meet with requirements of the following National and International standards, under the condition that appropriate industrial processing method are applied under a continuous quality control system and when used in combination with copolymer adhesive resin Lushan L-5R& polyethylene compound top coats EJ-1 and a compatible powder epoxy.

NFA 49710

CAN/CSA-Z245.21

DIN 30670S

Draft ISO 21809-1

General Information
Additive	Carbon Black (2%)
Features	Good Weather Resistance High Density
Uses	Oil/Gas Applications Pipe Coatings
Agency Ratings	CSA Z245.21 DIN 30670 ISO 21809-1 NF A 49-710
Appearance	Black
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	> 0.940	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
190°C/2.16 kg	> 0.17	g/10 min
190°C/5.0 kg	1.5 to 2.5	g/10 min
Carbon Black Content	> 2.0	%	ASTM D1603

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Break)	> 20.0	MPa	ASTM D638
Tensile Elongation ²(Break)	> 600	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -70.0	°C	ASTM D746
Vicat Softening Temperature	115	°C	ISO 306/A50
Melting Temperature	130	°C	ISO 11357-3

Note Message
1 .	50 mm/min
2 .	50 mm/min

Resin Grade	Manufacturer	Category	Trademark
Stat-Tech™ NN-20CF/000 Black	PolyOne Corporation	Nylon 66	Stat-Tech™
T-Blend® 6594B-G80E-A	TSRC Corporation	SEBS	T-Blend®
Evolue™-H SP4005	Prime Polymer Co., Ltd.	HDPE	Evolue™-H
KANEKA H305	Kaneka North America LLC	CPVC	KANEKA
OnForce™ LFT UR-50 LGF/000 Natural	PolyOne Corporation	PUR, Unspecified	OnForce™ LFT