Marlex® C513UV
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ahPxD_Marlex-C513UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® C513UV is a High Density Polyethylene material. It is available in Latin America or North America for blow molding or extrusion. Important attributes of Marlex® C513UV are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 5.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| 100% Igepal, Compression Molded, F50 | > 2000 | hr | ASTM D1693A |
| 100% Igepal, Compression Molded, F50 | > 2000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 700 | % | ASTM D638 |
| Flexural Modulus - Tangent 3(Compression Molded) | 1070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 4(Compression Molded) | 580 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 66.0 | °C | ASTM D648 |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 5 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Type S |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bakelite® MP 4165 | Hexion Inc. | Mel Phenolic | Bakelite® |
| Crastin® LW9320 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Delta MDPE 3512 | Delta Polymers | MDPE | Delta |
| Hostacom ERC213N 2 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Latilub 73/13 Y/20 | LATI S.p.A. | Acetal (POM) Copolymer | Latilub |