EMERGE™ PC 8600ECO-10 Advanced Resin contains 50% post consumer recycled (PCR) polycarbonate complying with IEEE 1680:2006 certified by TÜV Rheinland. It is a translucent and ignition resistant polycarbonate that does not contain chlorine, bromine, or phosphate additives to comply with global environmental standards. This resin combines good mechanical, thermal, and chemical properties while retaining excellent processability. Applications
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 61.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 66.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 5.0 | % | |
| Break, 3.20 mm, Injection Molded | 120 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 810 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525 1 |
| -- | 150 | °C | ISO 306/A120 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.550 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alcryn® 4070 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| BMC 610 Special | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Hyundai EP PPF HT310 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Hytrel® 4068 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| CYCOLAC™ DL100LG resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |