Moplen HP562T

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	LyondellBasell Industries
Trademark:	Moplen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3aWGoq_MoplenHP562T.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Homopolymer Resin for Spunbond Fiber

Features:

Very high melt flow with narrow MWD resin for high speed spin continuity of low denier fiber

Very uniform melt flow rate and low gel

Excellent processability

Good gas fading resistance

Applications:

Spunbonded nonwoven fabric using for hygiene products, medical, agriculture, geotextile, etc.

General Information
Features	Low speed solidification crystal point Homopolymer Resistance to gas fading Workability, good High liquidity Narrow molecular weight distribution
Uses	Spunbond nonwoven fabric Fiber
Processing Method	Fiber (spinning) extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.900	g/cm³	ASTM D792B
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	60	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	34.0	MPa	ASTM D638
Tensile Elongation (Yield)	10	%	ASTM D638
Flexural Modulus	1390	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	14	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	107	°C	ASTM D648

Resin Grade	Manufacturer	Category	Trademark
RTP 206 TFE 7	RTP Company	Nylon 66	RTP
TAISOX 2214	Formosa Plastics Corporation	LLDPE	TAISOX
OmniCarb™ PCGF10	OMNI Plastics, LLC	PC	OmniCarb™
SCHULAMID® 66 GF 30	A. Schulman Europe	Nylon 66	SCHULAMID®
LEXAN™ EXL1890T resin	SABIC Innovative Plastics	PC	LEXAN™