Delrin® 525GR NC000
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Zlg1M_Delrin-525GR-NC000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% Glass Reinforced Medium Viscosity Acetal Homopolymer |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.40 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 1.3 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.17 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 8500 | MPa | |
| 1000 hr | 6000 | MPa | |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 176 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 172 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.5E-5 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.70 | ||
| 1 MHz | 3.80 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission of Organic Compounds | 14.0 | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 AR 15 TFE 10 | RTP Company | Nylon 66 | RTP |
| Maxxam™ NS-818.G001-1032 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| POLYVIN® PVC 6620 | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| Vi-Chem PVC V221-70I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Kazan LDPE 16813-070 OKP 22 111 4102 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |