CALIBRE™ 303V-10
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ZVnIi_CALIBRE-303V-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 300V-10 Series polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. The CALIBRE 300V series products are available in 2 additive packages: CALIBRE 302V: UV stabilizer. CALIBRE 303V: Mold release and UV stabilizer. Products may be offered in colors. Please check for availability. Complies with:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) | |||
| -- | 10 | g/10 min | ASTM D1238 |
| 300°C/1.2 kg | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | |||
| 24 hr | 0.15 | % | ASTM D570 |
| 23°C, 24 hr | 0.15 | % | ISO 62 |
| Equilibrium | 0.32 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 2410 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | ASTM D638, ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 71.0 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus | |||
| -- | 2410 | MPa | ASTM D790 |
| -- 1 | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- 2 | 97.0 | MPa | ISO 178 |
| Yield | 96.5 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 45.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -- | 910 | J/m | ASTM D256 |
| 23°C | 35 | kJ/m² | ISO 180/4A |
| Unnotched Izod Impact | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact | 87.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 141 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 143 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 146 | °C | ASTM D1525, ISO 306/B50 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | 1.0E-3 | ASTM D150 | |
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Oxygen Index 4 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | |||
| -- | 1.586 | ASTM D542 | |
| -- | 1.586 1.586 | ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rulon® 1439 | Saint Gobain Performance Plastics | PTFE | Rulon® |
| RapidVac™ VA-288 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Adell Polyamide AR-36 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| ADMER™ QF551E | Mitsui Chemicals Europe GmbH | PP, Unspecified | ADMER™ |
| OP - PC - Unfilled GR912-VO | Oxford Polymers | PC | OP - PC - Unfilled |