HAIPLEN EP100 MF6
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ZKK5q_HAIPLEN-EP100-MF6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer high flow 33% mineral filled, high impact resistance and good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.70 - 0.90 | % | Internal method |
| Flow direction | 0.40 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 25 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 80 | J/m | ASTM D256 |
| 0°C | 110 | J/m | ASTM D256 |
| 23°C | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 80.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A50 |
| -- | 60.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 3(600°C) | 33 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 20,000 hr |
| 3 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 3727WZ | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Axpoly® PS01 3003 | Axion Polymers | PS (HIPS) | Axpoly® |
| Delrin® SC655 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Lupol® HG3200SK2 | LG Chem Ltd. | TPO | Lupol® |
| LNP™ THERMOCOMP™ QC006 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |