RTP 3499-3 X 92886
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3ZF0WQ_RTP-3499-3-X-92886.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermally Conductive - Electrically Conductive - Sloughing |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24100 | MPa | ASTM D638 |
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.40 | % | ASTM D638 |
| Flexural Modulus | 17900 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 59 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 232 | °C | ASTM D648 |
| Thermal Conductivity | |||
| -- 1 | 3.0 | W/m/K | ASTM E1530 |
| -- 2 | 18 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 332 - 366 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R66 | Spartech Plastics | PMMA+PVC | Royalite |
| Bergamid™ B650 G/Mi20 UF | PolyOne Corporation | Nylon 6 | Bergamid™ |
| HiFill® PBT 0175 A2 | Techmer Engineered Solutions | PBT | HiFill® |
| Vipel® F010-H2O-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| SCHULABLEND® (ABS/PA) M/MK 6501 | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |