POCAN® B 1205 XF 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3Ymsdu_POCANB1205XF000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding, improved flowability, improved impact strength |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.29 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 50.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 250°C, 2.00mm 1 | 2.1 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.30 | % | ISO 2577 |
| Flow direction : 250°C, 2.00mm 3 | 2.1 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.30 | % | ISO 2577 |
| Viscosity Number (Reduced Viscosity) | 100.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 2500 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 75.0 | MPa | ISO 178/A |
| 23°C 6 | 85.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 5.9 | % | ISO 178/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behavior 8 | passed | ISO 3795 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHMPR, 09-020 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 120 | kJ/m² | ISO 179/1eU |
| 23°C | 140 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 90 | kJ/m² | ISO 180/1U |
| 23°C | 110 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 | °C | ISO 306/B120 |
| Melting Temperature 9 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 981 TFE 5 | RTP Company | PSU | RTP |
| Sanren F280 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| SEETEC EVA VS440 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| KumhoSunny ASA XC230 | Shanghai KumhoSunny Plastics Co., Ltd. | ASA | KumhoSunny ASA |
| Karina IVORY PVC COMP. 105908-35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |