LNP™ LUBRICOMP™ PDXF89080 compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3YhAqk_LNP-LUBRICOMP-PDXF89080-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-F-89080 Product reorder name: PDXF89080 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.918 | g/cm³ | |
| -- | 0.920 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 204 | MPa | ASTM D638 |
| -- | 246 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 10.0 | MPa | ASTM D638 |
| Yield | 9.00 | MPa | ISO 527-2/5 |
| Break 3 | 9.00 | MPa | ASTM D638 |
| Break | 8.00 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 73 | % | ASTM D638 |
| Yield | 88 | % | ISO 527-2/5 |
| Break 5 | 90 | % | ASTM D638 |
| Break | 160 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 123 | MPa | ASTM D790 |
| -- 7 | 129 | MPa | ISO 178 |
| Flexural Stress | 5.60 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D256 |
| 23°C 8 | 37 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 19.4 | J | ASTM D3763 |
| -- | 19.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 42.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 41.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 23.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 23.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-3082S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| NEXT SIGNATURE CAB MG-100 | NEXT Specialty Resins, Inc. | CAB | NEXT SIGNATURE |
| Hostacom X 454 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Iupital® A25-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| ALTECH® PP-B ECO 2030/500 GF30 | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |