LNP THERMOCOMP RX96592 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-R-96592 Product reorder name: RX96592 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 1.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.85 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 10200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 154 | MPa | ASTM D638 |
| Break | 152 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.2 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9140 | MPa | ASTM D790 |
| -- 5 | 8810 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 218 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 222 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 67 | J/m | ASTM D256 |
| 23°C 8 | 6.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 630 | J/m | ASTM D4812 |
| 23°C 9 | 38 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.50 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 253 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 239 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 233 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 9.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218 V40 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| VITAMIDE® BR3X | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| DOMAMID® 6G15H | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| REV Materials 8002-001 | REV Materials | PP, Unspecified | REV Materials |
| Sylvin 2990-76 Blue 8474 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |