TRIBOCOMP® PBT CF30 TS0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3YGB33_TRIBOCOMP-PBT-CF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PBT CF30 TS0 is a polybutene terephthalate (PBT) product, which contains 15% ptfe fiber and 30% carbon fiber reinforced materials. It is available in Europe. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 19000 | MPa | ISO 527-2 |
| 90°C | 11500 | MPa | ISO 527-2 |
| 120°C | 10000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 140 | MPa | ISO 527-2 |
| Fracture, 90°C | 85.0 | MPa | ISO 527-2 |
| Fracture, 120°C | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.14 | ASTM D3702 | |
| Static | 0.12 | ASTM D3702 | |
| Wear Factor | 8.00 | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 1.8E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.55 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 | ohms | ASTM D257 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 220 - 260 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | < 270 | °C | |
| Mold Temperature | 70.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® MED 3014-0180 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| TABOND 3047 | SILON s.ro | LLDPE | TABOND |
| Colorite Rigid PVC 2600 UVLCR | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Karina BLACK PVC COMPOUND 800-48/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Starex GR-4005 | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |