LEXAN™ LUX9616G resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3XVRW9_LEXAN-LUX9616G-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN LUX9616G (EXRL0945) is a UV stabilized high viscosity, flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effect and thin wall FR performance providing good colorstability under heat exposure. Developed for LED applications. It meets WEEE/RoHS requirements for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2230 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Break 3 | 65.0 | MPa | ASTM D638 |
| Break | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 80 | % | ASTM D638 |
| Break | 75 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2160 | MPa | ASTM D790 |
| -- 7 | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 9 | 15 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 123 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 141 | °C | ASTM D1525 12 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C | |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 1.50 mm | 850 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218G1 V25 BLACK 34 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Alpha PVC GW 3026 NAT.LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| PENTAMID A GV20 GK10 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Osterlene® HD0752 | Osterman & Company | HDPE | Osterlene® |
| Hylex® P1003L2 HB | Entec Polymers | PC | Hylex® |