Petrotene® PP A3 G40 HF CNZ0207 PH353
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3XG2PS_Petrotene-PP-A3-G40-HF-CNZ0207-PH353.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene with 40% fiberglass, chemically coupled, ideal for injection molding, resistant to oil, grease and many solvents, has a high tensile strength and higher HDT, and excellent stability dimensional, and higher impact. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 to 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.35 to 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.040 to 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5400 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Continuous Use Temperature | 100 | °C | |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 42 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 35.0 to 65.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PBT-15GF | Polymer Technology and Services, LLC | PBT | PTS |
| SCHULADUR® A MV 14 SHI FR 1(f1) black 96.8106 | A. Schulman Europe | PBT | SCHULADUR® |
| Sindustris PP GP3201 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TEKANATE™ G715FR | Mando Advanced Materials Co., Ltd. | PC | TEKANATE™ |
| apigo bio® CM 680 | API SpA | TPO (POE) | apigo bio® |