RTP 2283 LF

Category: PEEK , Polyetheretherketone
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 3XCfgt_RTP-2283-LF.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Carbon Fiber - Low Flow
General Information
Filler / Reinforcement
  • Carbon fiber reinforced material, 20% filler by weight
Features
  • Low liquidity
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.36g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.10%ASTM D955
Moisture Content 0.10%
Additional InformationNominal ValueUnit
Primary Additive 20%
MechanicalNominal ValueUnitTest Method
Tensile Modulus 20000MPaASTM D638
Tensile Strength 221MPaASTM D638
Tensile Elongation (Yield)1.8%ASTM D638
Flexural Modulus 17200MPaASTM D790
Flexural Strength 331MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)85J/mASTM D256
Unnotched Izod Impact (3.20 mm)750J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)316°CASTM D648
ElectricalNominal ValueUnitTest Method
Volume Resistivity < 1.0E+5ohms·cmASTM D257
FlammabilityNominal ValueUnitTest Method
Flame Rating (1.50 mm, ** Values per RTP Company testing.)V-0UL 94
InjectionNominal ValueUnit
Drying Temperature 149°C
Drying Time 3.0hr
Dew Point -28.9°C
Processing (Melt) Temp 349 - 399°C
Mold Temperature 163 - 218°C
Injection Pressure 82.7 - 124MPa
Injection instructions
Desiccant Type Dryer Required.
Resin Grade Manufacturer Category Trademark
Vydyne® R533H BK0667 Ascend Performance Materials Operations LLC Nylon 66 Vydyne®
Akulon® S223-HG7 DSM Engineering Plastics Nylon 66 Akulon®
Fainplast PVC RKS 205/K Fainplast Compounds S.r.l PVC, Rigid Fainplast PVC
LUVOCOM® 80-8030 VP Lehmann & Voss & Co. Acetal (POM) Copolymer LUVOCOM®
Sylvin 6221-83 Green 3199 Sylvin Technologies Incorporated PVC, Unspecified Sylvin