HOPELEX TC-8001G
| Category: | PC , Polycarbonate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3WybmT_HOPELEX-TC-8001G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermal conductive, graphite filled, medium viscosity, easy mold release Non-brominated, non-chlorinated flame retardant Available in opaque color only |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 46.1 | MPa | ASTM D638 |
| Flexural Modulus 2 | 5300 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 65.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Thermal Conductivity 4 | > 0.60 | W/m/K |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 290 to 310 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| 4 . | Hot Wire Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 2408 HSSP BK | Custom Resins Group | Nylon 6 | Nylene® |
| FHR Polypropylene P9R2M-062 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Hostacom TRC 160N HF Natural | LyondellBasell Industries | PP Copolymer | Hostacom |
| Pinnacle PP 6135C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |
| LNP™ LUBRICOMP™ LCL36E compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |