Quadrant EPP Fluorosint® 500
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3VaGOR_Quadrant-EPP-Fluorosint-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Fluorosint® 500 is a Polytetrafluoroethylene (PTFE) product filled with mica. It is available in Europe or North America. Applications of Quadrant EPP Fluorosint® 500 include engineering/industrial parts, electrical/electronic applications and sealing applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.32 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.10 | % | |
| Saturation, 23°C | 3.0 | % | |
| Water Absorption 1(23°C, 3.00 mm) | 14.0 | mg | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 10.0 mm) | 55 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 8.00 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/1B/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 2 | 260 | °C | |
| -- 3 | 280 | °C | |
| Melting Temperature (DSC) | 327 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 4.5E-5 | cm/cm/°C | |
| 23 to 150°C | 4.5E-5 | cm/cm/°C | |
| > 150°C | 6.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.77 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 11 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.85 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 8.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | > 95 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Weight, 24 hrs |
| 2 . | 20000 hrs |
| 3 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PA66 910/1.1 AR10 CF10 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Delta N6-100 | Delta Polymers | Nylon 6 | Delta |
| Goodfellow PHB Biopolymer (PHB) | Goodfellow Corporation | Biodeg Polymers | Goodfellow PHB |
| Grilamid® 2S 25 W 20 X nat | EMS-GRIVORY | Nylon 610 | Grilamid® |
| LNP™ THERMOCOMP™ RX06420 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |