RTP 1505-72D
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3UlwzQ_RTP-1505-72D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5170 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3590 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 199 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 168 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 3mil/in.Flammability, ASTM D-635: B in/min. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 193 - 221 | °C | |
| Middle Temperature | 193 - 221 | °C | |
| Front Temperature | 193 - 221 | °C | |
| Mold Temperature | 23.9 - 51.7 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E F2201 | Asia Polymer Corporation (APC) | LDPE | Polymer-E |
| SEPAZ™ LB30 | Mando Advanced Materials Co., Ltd. | Nylon 6 | SEPAZ™ |
| Fainplast PVC KL 93/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lumid® HI5083A(W) | LG Chem Ltd. | Nylon 6+ABS | Lumid® |
| Ultramid® B24 N 02 | BASF Corporation | Nylon 6 | Ultramid® |