UBE Nylon 5034 FDX40 Datasheet,Nylon 66/6,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
UBE NYLON 5034 FDX40 is a high viscosity, nucleated Polyamide 6/6.6 copolymer. The material is suitable for cast film and air-cooled blown film production. Typical application is for shrink bags and pouches.

General Information
Additive	Nucleating agent
Features	Nucleated Workability, good Low shrinkage Definition, high Viscosity, High
Uses	Films Bags cast film Shrinkable film
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	1.0	ASTM D1894
With Self-Static	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	400	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	24.0	MPa	ASTM D882
Fracture, extruded film	115	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	650	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	197	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	155		ASTM D523
Haze	< 0.50	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 40 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.89Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 80/20Water Vapor Permeability, JIS Z0208: 125 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <10 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <10 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 40 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 3.89Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 80/20Water Vapor Permeability, JIS Z0208: 125 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <10 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <10 hole/0.04 m²

Resin Grade	Manufacturer	Category	Trademark
Quadrant EPP Nylatron® NSM	Quadrant Engineering Plastic Products	Nylon 6	Quadrant EPP
RAMTOUGH PZ509	Polyram Ram-On Industries	PC	RAMTOUGH
LNP™ THERMOCOMP™ JF002 compound	SABIC Innovative Plastics	PESU	LNP™ THERMOCOMP™
PermaStat® 100 HI	RTP Company	PP, Unspecified	PermaStat®
Crastin® LW9320LM BK591	DuPont Performance Polymers	PBT	Crastin®

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	3UbQDZ_UBE-Nylon-5034-FDX40.pdf
PRICE:	Order Products email sales@su-jiao.com