ExxonMobil™ LDPE LGA 105
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 3UYGAx_ExxonMobil-LDPE-LGA-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LGA 105 is a homopolymer with good transparency, washability and dry cleaning film resin, which can be used to produce very low thickness ductile films. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD | 168 | MPa | ASTM D882 |
| TD | 199 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 9.20 | MPa | ASTM D882 |
| TD : Yield | 9.23 | MPa | ASTM D882 |
| MD : Fracture | 20.8 | MPa | ASTM D882 |
| TD : Fracture | 18.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 390 | % | ASTM D882 |
| TD : Fracture | 680 | % | ASTM D882 |
| Dart Drop Impact | 76 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 440 | g | ASTM D1922 |
| TD | 200 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 82 | ASTM D2457 | |
| Haze | 4.3 | % | ASTM D1003 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 30 FR 2 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Vynaprene 7907 | Axiall Corporation | PVC, Rigid | Vynaprene |
| Badamid® LB70 GF/GK30 | Bada AG | Nylon 6 | Badamid® |
| Hybrid PC/ABS 120 BK | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| AURUM® PI-PA | Mitsui Chemicals, Inc. | PI, TP | AURUM® |